Tungsten Alloy Military Swaging Rod
Tungsten Alloy Military Swaging Rod Tungsten Alloy Military Swaging Rod

Tungsten Alloy Military Swaging Rod

Item No.: 012
Swaging greatly increases tungsten alloy rod's ultimate tensile strength. The ultimate tensile strength of regular tungsten alloy rod is 1050 MPa . However, after swaging, the ultimate tensile strength can reach 1200 MPa min, we can even control tungsten
INQUIRY PDF Format
Buy At WishBuy At Alibaba
Description Tungsten Alloy Swaging Rod for Military Video

Tungsten Alloy Military Swaging Rod

 
Swaging greatly increases tungsten alloy rod's ultimate tensile strength. The ultimate tensile strength of regular tungsten alloy rod is 1050 MPa . However, after swaging, the ultimate tensile strength can reach 1200 MPa min, we can even control tungsten alloy military swaging rod at 1400 MPa. Tungsten alloy military swaging rod is one of our main products. The composition of tungsten alloy military swaging rod is 93%WNiFe. Our common types:
Diameter: 12mm~20mm, Length: less than 400mm; Diameter: 20mm~400mm, Length: less than 500mm.
We can manufacture other products according to customers' specific requirements.
 15.8 - 18.75 g/cm3, 20 - 35 Tungsten Alloy Swaging Rod for Military; Tungsten Alloy Rod Used In The FJFB-3 3-die Set Contiguity and hardness variation in sintered, heat-treated and swaged tungsten alloy.
Tungsten Alloy Swaging Rod Main Properties :
 
*  High density
*  High melting point
*  Small volume
*  Excellent hardness
*  Superior wearing resistance
*  High ultimate tensile strength
*  High ductility
*  High temperature resistance
*  Low vapor pressure
 
 

Military Application of Tungsten Alloy Swaging Rod

 
Tungsten alloy swaging rod can be used in military defense, such as depleted uranium kinetic energy penetrators, bullet, armor piercing, armor piercing bullets, sniper rifle penetrator, etc.

Main Processing of Tungsten Alloy Swaging Rod:

 
1). Mixing
2). Pressing
3). Sintering
4). Heat treatment
5). Swaging
6). Machining
Repeated heat treatment and swaging is performed need at least several times.
In this way, tungsten alloy swaging rod can be improved at tensile strength as well decrease elongation and impact toughnes.
 

Tungsten Alloy Swaging Military Rod Properties Table

 
 
Composition		  
Processing		 Density
 
g/cm3		 Tensile strength
 
Min. Mpa		 Elongation
 
Min.%		 Hardness
 
Min. HRC		 Impact Energy
 
J/cm2
90WNiFe Heat treatment 17.10±0.15 1000-1100 18-29 25-29 170
 
92.2WNiFe		 Heat treatment  
17.60±0.15		 900-1000 15-25 25-29 170
Swaging 1300-1500 8-18 35-45 120
91.7WNiFe Heat treatment 17.65±0.15 1000-1100 15-25 25-29 170
93 WNiFe Heat treatment 18.10±0.10 900-1000 15-25 25-30 160
94 WNiFe Heat treatment 17.90±0.10 900-1000 15-25 25-30 160
 
95 WNiFe		 Heat treatment  
18.10±0.15		 900-1000 12-20 25-31 160
Swaging 1300-1450 6-12 35-45 120
 
96 WNiFe		 Heat treatment  
18.30±0.15		 900-1000 12-18 25-31 160
Swaging 1300-1450 6-12 35-45 120
97 WNiFe Heat treatment 18.3±0.15 800-900 9-13 28-31 130